Selection of peptides binding to metallic borides by screening M13 phage display libraries

BMC Biotechnology volume 14, Article number: 12 (2014) Cite this article

Abstract

Background

Metal borides are a class of inorganic solids that is much less known and investigated than for example metal oxides or intermetallics. At the same time it is a highly versatile and interesting class of compounds in terms of physical and chemical properties, like semiconductivity, ferromagnetism, or catalytic activity. This makes these substances attractive for the generation of new materials. Very little is known about the interaction between organic materials and borides. To generate nanostructured and composite materials which consist of metal borides and organic modifiers it is necessary to develop new synthetic strategies. Phage peptide display libraries are commonly used to select peptides that bind specifically to metals, metal oxides, and semiconductors. Further, these binding peptides can serve as templates to control the nucleation and growth of inorganic nanoparticles. Additionally, the combination of two different binding motifs into a single bifunctional phage could be useful for the generation of new composite materials.

Results

In this study, we have identified a unique set of sequences that bind to amorphous and crystalline nickel boride (Ni3B) nanoparticles, from a random peptide library using the phage display technique. Using this technique, strong binders were identified that are selective for nickel boride. Sequence analysis of the peptides revealed that the sequences exhibit similar, yet subtle different patterns of amino acid usage. Although a predominant binding motif was not observed, certain charged amino acids emerged as essential in specific binding to both substrates. The 7-mer peptide sequence LGFREKE, isolated on amorphous Ni3B emerged as the best binder for both substrates. Fluorescence microscopy and atomic force microscopy confirmed the specific binding affinity of LGFREKE expressing phage to amorphous and crystalline Ni3B nanoparticles.

Conclusions

This study is, to our knowledge, the first to identify peptides that bind specifically to amorphous and to crystalline Ni3B nanoparticles. We think that the identified strong binding sequences described here could potentially serve for the utilisation of M13 phage as a viable alternative to other methods to create tailor-made boride composite materials or new catalytic surfaces by a biologically driven nano-assembly synthesis and structuring.

Background

The diverse group of transition metal borides comprises compounds that exhibit or combine interesting physical properties such as semiconductivity, ferromagnetism, hardness, thermal and mechanical stability and oxidation resistance [1]. Some of the binary, ternary, and quaternary metal borides are even superconducting or represent some of the strongest permanent magnets [2, 3]. Because of the high melting point of boron, the traditional synthesis of metal borides does not result in nanoscale or nanostructured products. As an alternative, a room temperature synthesis of nickel boride nanoparticles via hydrolysis of NaBH4 has been reported [4–7]. Biological systems, on the other hand, can synthesise materials under mild and environmentally benign conditions [8]. Nickel borides like Ni3B, Ni2B or NiB are considered to exhibit catalytic activity in all kinds of reduction reactions, and hydrogenation reactions [9–15]. Like iron borides they are expected to exhibit paramagnetism, ferro- or superparamagnetism [16, 17]. The electrical conductivities of different nickel borides vary with their boron content. Thus, the nickel-boron system represents an interesting class of compounds for a model study on peptide-boride interactions and the potential of bio-modified inorganic solids. Until now nothing is known about the interaction between boron-containing materials and peptides, although peptides binding to solid surfaces have been extensively exploited for other chemical systems in nanoscale science because of their material selective properties [18–20]. To select for peptides that are capable of interacting with inorganic materials, phage peptide display is a powerful technique [21]. Phage display is a selection technique in which a combinatorial library of random peptides (~109) is expressed as a fusion with an M13 phage coat protein (usually p3), resulting in the display of the fused peptide on the surface of the phage particle. Selection of the desired peptides, which is usually a random 7- or 12-amino acid peptide, is achieved by multiple rounds of target binding, elution and amplification, a process known as biopanning (or panning). Because the DNA sequence for the displayed peptide is genetically fused to the p3 gene, the amino acid sequence of the phage-displayed peptide is readily obtained by sequencing the p3 encoding DNA.

Phage display has been used to identify peptides which specifically bind to metals like Ag, and Pd, and various inorganic materials like ZnO, SiO2, TiO2, ZnS, and CdS [22–29]. In the last few years, specific binding peptides to nickel have also been described [30–32]. Up to now, no specific binding peptides have been identified for borides in general, neither nanostructured nor bulk material, or more specifically nickel boride nanoparticles. The identification of such a selective binding peptide sequence would be a first, significant step towards peptide-modified boride materials and composites. Such linkers would help to make boride particles available for biological systems and allow for a tuning of the properties of borides using a biological peptide-enabled nano-assembly process.

Since to our knowledge no binding peptides to boride nanoparticles are described in the literature, our aim of this research was to identify peptides that bind specifically to metallic borides. This constitutes the first step in order to combine two different binding motifs e.g. a metallic and a ceramic boride into a single bifunctional phage or into a synthetic bifunctional peptide. This would be useful for the generation of new boride composite materials in which the physical properties of two different borides are unified which is until now not combinable. Peptides were selected after several rounds of screening with a commercial phage library. Several Ni3B-binding peptides were selected using nanoparticles of amorphous and crystalline Ni3B as targets. From the initial library, we identified ten phages that exhibit selective binding to either amorphous or crystalline or both using titer count analysis, fluorescence and atomic force microscopy.

Results and discussion

Isolation of Ni3B-binding peptides

To identify Ni3B-binding peptides, a commercial available M13 bacteriophage display library (Ph.D.-7; New England Biolabs) was screened against amorphous and crystalline Ni3B nanoparticles. In the Ph.D.-7 library, random linear heptapeptides are displayed as N-terminal fusions to the minor coat protein p3 of M13. The M13 phage p3 constructs used in the screening selection have five copies of the peptide displayed on the one end of the phage particle. Five rounds of biopanning were conducted for each of the amorphous and crystalline Ni3B substrates. Each biopanning round involved the steps of phage binding, removal of weak binding affinity phage by washing, and elution of bound phage by a rapid pH decrease. More stringent washing conditions were used in the additional rounds of panning. A 0.3% TBST wash solution was used to remove phage with low binding affinity to Ni3B during the second round, whereas 0.5%, 0.6%, and 0.8% TBST wash solutions were used for the third, fourth, and fifth round, respectively. A total of 58 phage clones were selected and analysed by DNA sequencing after the fourth and fifth round of biopanning against amorphous and crystalline Ni3B substrates. For amorphous Ni3B substrates, 30 peptides were identified coding for 15 different peptide sequences (designated with an A for amorphous). A summary of the peptides identified from biopanning against amorphous Ni3B is provided in Table 1. In the case of the biopanning against crystalline Ni3B substrates, 28 peptides were isolated coding for 28 different peptide sequences (designated with a C for crystalline) shown in Table 2. The fact that all the peptides which were identified for crystalline Ni3B are different, could be an indication of a more complex surface structure for crystalline Ni3B nanoparticles than for amorphous Ni3B nanoparticles. Interestingly, one peptide sequence, ANHQSAN, termed A6/C28, was isolated from both, amorphous and crystalline, Ni3B substrates. While most of the peptides, especially identified for the crystalline Ni3B substrate, were isolated only once, for the amorphous substrate the peptide A1 was isolated eight-times, A2 six-times, and A3 four-times, respectively.

Table 1 Summary of the isolated binding peptides to amorphous Ni 3 B
Full size table
Table 2 Summary of the isolated binding peptides to crystalline Ni 3 B
Full size table

Characteristics of the identified binding peptides

Due to the fact that cysteines interfere with the p3-mediated M13 infection process, no cysteines were present in the identified binding peptides [33]. The binding peptides showed approximately three-times more positively charged residues (K, R, and H) than negatively charged residues (D and E) (Table 3). Compared with the peptides binding to amorphous Ni3B, the binding peptides to crystalline nickel boride show a two-times higher occurrence of the positively charged amino acids arginine and lysine, and a three-times higher occurrence of histidine, respectively. Although the distribution of charged amino acids in the library is comparable in frequency, the increased abundance of these amino acids within the identified sequences could be possibly attributed to the surface composition of the nickel borides. The characterisation of the surface of different amorphous nickel borides by Okamoto et al. and Caputo et al. by X-ray photoelectron spectroscopy (XPS) and X-ray diffraction (XRD), respectively, revealed that the electron densities on nickel are increased by electron transfer from boron to the metal [6, 34]. Based on the shift of the charge, specific binding peptides could therefore interact with the nickel boride substrates via electrostatic interactions. The majority of the peptides identified on Ni3B prevalently possess alanine, leucine, proline, serine and threonine residues (Figure 1) which is a consequence of the amino acid distribution of the applied phage display library. In addition, the binding peptides identified on amorphous Ni3B possess 2.5-times more asparagine residues as compared with the peptides identified on crystalline Ni3B. This is vice versa with proline residues binding to crystalline Ni3B. The strong presence of asparagine in the peptide sequences binding to amorphous Ni3B, and asparagine and histidine in the peptide sequences binding to crystalline Ni3B suggests that the binding between the Ni3B and peptides could furthermore occur via hydrogen bonding interactions. The almost complete absence of tryptophan, phenylalanine, and methionine residues is also due to the low frequencies of these amino acids within the library. An amino acid position consensus was not evident from the 7-mer library screening of Ni3B nanoparticles as substrates. However, besides the predominantly hydrophobic amino acids (A and L) and hydrophilic amino acids (S and T) the variety of amino acids with charged side groups implies that these groups could be essential in specific binding to both substrates via electrostatic interactions. The Ni3B-binding peptides identified possess calculated theoretical isoelectric points (pI) ranging from strongly acidic (4.0) to highly basic (9.75). 60% of the peptides binding to amorphous Ni3B show a pI value < 7.5 while 40% of the peptides have pI > 7.5. 57% of the peptides binding to crystalline Ni3B show a pI value < 7.5 and 43% of the peptides have pI > 7.5. Therefore the identified peptides can be grouped into the categories acidic (pI 3.0 - 5.9; 35.7% of the peptides), neutral (pI 6.0 – 8.9; 52.4% of the peptides), and basic (pI 9.0 – 12; 11.9% of the peptides), respectively.

Table 3 Occurrences of amino acids of the isolated Ni 3 B binding peptides
Full size table
Figure 1
figure 1

Amino acid distribution of the isolated peptide sequences. A total of 15 peptide sequences were analysed for amorphous Ni3B (grey bars) and a total of 28 peptide sequences were analysed for crystalline Ni3B (black bars).

Full size image

Relative binding affinity experiments

Because of the heterogeneity of all of the identified binding peptides and the absence of a distinctive binding motif, the binding strength of each of the 42 identified peptides to amorphous (Figure 2A) and crystalline (Figure 2B) Ni3B was determined by titer assays. Since previously binding affinity experiments at pH 5 or pH 9 with a subset of the identified binding peptides showed no increase in binding affinity (data not shown) the relative binding affinity experiments were carried out at pH 7. As a control to verify that the peptide was the interactor of interest, M13KE wild-type (M13wt) phage without a random peptide insert were compared in the same manner as the peptide clones. As presented in Figure 2A, most of the phage clones, except C2 and C17, bind to amorphous Ni3B with greater affinity than does the M13wt phage, which shows a binding affinity of 2 × 107 pfu/ml with amorphous Ni3B. Compared with the M13wt phage, 9 out of 42 identified peptides (see arrows in Figure 2A) bound on average 100-times and 28 on average ten-times more efficiently to amorphous Ni3B than the wild-type, verifying that binding to the substrate was a result of the peptide sequence and not due to non-specific phage coat protein interactions. The peptides A7, C12, and C15 (see arrows in Figure 2B) bound on average 1000-times more efficiently to crystalline Ni3B as compared to the M13wt phage, which shows a binding affinity of 5 × 106 pfu/ml. Interestingly, the phage clone A7 identified for amorphous Ni3B shows a higher binding affinity to crystalline Ni3B than most of the Ni3B-binding peptides (C1-C11, C13-C14, and C16-C28) identified for crystalline Ni3B. In addition, the amorphous Ni3B-binding peptides A8-A10 show a higher binding affinity to crystalline Ni3B (≥109 pfu/ml) than several binding peptides found for crystalline Ni3B specifically (i.e. C1-C11, C13-C14, C16-C24, and C27-28). The relative binding affinity experiments revealed a set of several strong binders (>109 pfu/ml) for amorphous (A1-A3, A7, C4, C9, C13, C15, and C24) and crystalline (A7, C12, and C15) substrates (Table 4). The phages displaying the peptides A7 and C15 emerged as the best binders for both substrates.

Figure 2
figure 2

Evaluation of the binding strength of each of the 42 identified phage clones. The relative binding affinity of the phage clones to amorphous (A) and crystalline (B) Ni3B nanoparticles was determined by titer assays at pH 7. The assay was repeated three-times for each clone and the elucidated phage amounts were arithmetically averaged. As a control, M13KE wild-type (M13wt) phage without a random peptide insert were compared in the same manner as the phage clones. Strong binding phage clones (> 109 pfu/ml) are indicated with an arrow. Clones identified on amorphous Ni3B are designated with an A, clones identified on crystalline Ni3B are designated with a C.

Full size image
Table 4 Strong binders identified by relative binding affinity experiments
Full size table

Competitive binding assays of the best binding peptides

The competitive binding assay represents a method to determine the most selective binding peptide sequence from a large subset of phage display results [35]. To identify a specifically recognised structural correlation between the surfaces of amorphous and crystalline Ni3B nanoparticles, the individual phage clones of the nine strongest binders (A1-A3, A7, C4, C9, C13, C15, and C24) to amorphous Ni3B as determined by the relative binding affinity experiments were diluted into a single mini-phage library. The mini-phage library was then screened against amorphous or crystalline Ni3B substrates. To receive better statistical results, the competitive binding assays were repeated three-times. After a single panning experiment, the strongly bound phages were isolated and a total of 58 phage clones were randomly selected and analysed by DNA sequencing to identify the strongest binding peptides. In Tables 5 and 6 the most abundant sequence indicates the strongest binding peptide to amorphous and crystalline Ni3B, respectively. Among the 58 randomly chosen plaques, the phage displaying the A7 peptide LGFREKE has the strongest binding affinity to amorphous (seventeen-times, ~58%) and crystalline (thirteen-times, ~45%) Ni3B. Interestingly, the amino acids lysine, arginine, and glutamic acid were shown to have a pronounced adhesion of their charged side groups to amorphous Si3N4 and SiO2 under aqueous conditions [36]. It was also reported, that the surface of amorphous Si3N4 may present negative sites in solution [37]. Therefore substrates, possessing negatively surface charges in aqueous solution with pH values less than the intrinsic pKa of the side chain of a basic amino acid, a peptide containing basic amino acids will be positively charged at these groups and will provide an attractive interaction to the given surface [36]. In aqueous solutions with higher pH values than the intrinsic pKa of the side chain of an acidic amino acid, a peptide containing acidic amino acids will be negatively charged at these groups. Based on these facts, the best binder A7 (LGFREKE) possesses in solution at pH 7 an alternating series of positively and negatively charged side chains in its peptide sequence which could be responsible for an interaction between the charge depleted boron and the electrons accumulated on the nickel side of amorphous and crystalline Ni3B nanoparticles. In contrast, the 7-mer peptide sequence TNLTLAS, termed A1, which emerged as the dominant amorphous Ni3B binder in the initial screening, possesses no charged side chain. The lack of electrostatic interactions might contribute to the observed fact, that it does not show the highest frequency in the competitive assay.

Table 5 Competitive binding assay results for amorphous Ni 3 B target
Full size table
Table 6 Competitive binding assay results for crystalline Ni 3 B target
Full size table

Fluorescence microscopy of Ni3B-M13 complex

The binding of phage displaying the A7 peptide LGFREKE to amorphous and crystalline Ni3B nanoparticles was confirmed by fluorescence microscopy. Amplified phage displaying the LGFREKE peptide were incubated either with amorphous or crystalline Ni3B nanoparticles and then washed to remove the nonspecifically bound phage particles. The samples were then dyed using a fluorescently tagged anti-M13 monoclonal antibody and washed again to eliminate nonspecifically bound anti-M13 antibodies. The fluorescence confocal images in Figure 3A and C show the LGFREKE displaying phage binding to the surface of amorphous and crystalline Ni3B nanoparticles, respectively. Considerable fluorescence emits from the surfaces of the LGFREKE phage-Ni3B nanoparticles. Although the relative binding affinity experiments showed an unspecific binding of the wild-type phage to the Ni3B substrates, the control experiments (Figure 3E and G) showed no fluorescence. This could be due to the fact that the concentration of bound phage is below the detection limit.

Figure 3
figure 3

Analysis of the phage binding by fluorescence microscopy. Confocal fluorescence (A, C) and transmission optical microscopy (B, D) of LGFREKE phage bound to amorphous (A, B) and crystalline (C, D) Ni3B nanoparticles. The samples were dyed using a fluorescently tagged anti-M13 monoclonal antibody. Confocal fluorescence (E, G) and transmission optical microscopy (F, H) of the control experiments of amorphous and crystalline Ni3B nanoparticles, respectively, which were preincubated with M13KE wild-type (M13wt) phage before incubation with the fluorescently tagged antibody.

Full size image

AFM measurements

To verify the interaction between M13 phage displaying the A7 peptide on the p3 coat protein and Ni3B particles, AFM measurements of phage bound to amorphous and crystalline Ni3B particles were carried out (Figure 4). The modified M13 phage were incubated either with amorphous or crystalline nanoparticles as shown in Figure 4A and B, respectively. As shown in Figure 4A and B the height of the colour scale exceeds the height of the particles. This colour scale was chosen to show the 100-nm-thick particles together with the 6-nm-thick phage. Individual phage are approximately 1 μm in length and 6.5 nm in height. This cross section and length of the modified phage correspond to that of M13 wt phage (data not shown). Some phage were oriented with their ends towards a nanoparticle (see arrows in Figure 4), which implies an affinity between the modified phage proteins and the particle. There are a few particles that seem to be attached to the unmodified side of the phage. Possible explanations for this observation include unspecific interaction or the presence of more than one phage, i.e. bundles of phage where the end of one phage coincides with the side of another phage. A small level of unspecific interaction between nanoparticles and phage cannot be avoided during preparation for AFM imaging. The phage oriented with their ends towards the nanoparticles, suggest that the peptide LGFREKE interacts with both amorphous and crystalline Ni3B nanoparticles.

Figure 4
figure 4

Visualisation of the phage binding by atomic force microscopy. Topographic AFM images of the binding of modified M13 phage (LGFREKE) to amorphous (A) and crystalline (B) Ni3B nanoparticles. The AFM images of M13 phage displaying the A7 peptide on p3 showed the phage to bind to several amorphous and crystalline Ni3B nanoparticles at the tip of p3, which are indicated by arrows. The colour scale exceeds the particle height to better display the particle cross section.

Full size image

Conclusions

Metal borides are inorganic solids that are very interesting due to their high versatility in physical properties, as for example magnetism, electrical and thermal conductivity, hardness and catalytic activity, but at the same time they are difficult to prepare. Besides the application as catalysts in all kinds of reduction reactions, and hydrogenation reactions, metallic borides are employed for the generation of conductive ceramics, hard magnets, superconductors, and hard materials [9–15, 38–40]. Typical synthesis routes employ high reaction temperatures and do not allow for a directed synthesis of particles that are well-defined in terms of size, shape, uniformity, phase purity, or crystallinity. Formation of metal boride nanoparticles in solvents has been described occasionally, but an interaction of borides with biological material or bio-molecules like peptides was unknown before [4, 5]. To the best of our knowledge, the present study is the first to identify peptides that bind specifically to amorphous and to crystalline Ni3B nanoparticles. Although all identified peptide sequences showed no significant binding motif, the analysis of the resulting Ni3B-binding sequences found them to be enriched in charged amino acids. The identified binding sequences possessed approximately three times more positively charged than negatively charged amino acids which leads to the assumption of electrostatic interactions between the identified binding peptides and the Ni3B substrates. Fluorescence microscopy and AFM studies directly confirmed the adhesion of the best binding phage displaying the peptide LGFREKE to amorphous and crystalline Ni3B particles. The best binding peptide sequence could play an important role for the development of a new synthesis route of Ni3B in the presence of phage displaying the peptide, or the synthetic peptide, respectively, which would represent a complete new approach. The synthesis of Ni3B in the presence of LGFREKE could result in mono-disperse and peptide capped nanoparticles with well-defined and uniform sizes and shapes exhibiting new catalytic and magnetic properties. Furthermore, the utilisation of M13 phage as template for the Ni3B mineralisation could potentially serve as a viable alternative to create tailor-made boride composite materials by a biologically driven nano-assembly synthesis and structuring for the generation of thermoelectric devices and field effect transistors.

Methods

Phage and bacteria strains

Recombinant M13 phage from the Ph.D.-7 heptapeptide library (New England Biolabs, MA) were amplified and propagated in the E. coli host strain ER2738 (F', lacIq, Δ(lacZ)M15, proA+B+,zzf::Tn10(TetR)/fhuA2, supE, thi-1, Δ(lac-proAB), Δ(hsdS-mcrB)5, [rk-mk-McrBC-]), as described by the manufacturer. M13KE wild-type (M13wt) phage was used for the determination of unspecific binding to the Ni3B targets. Bacteria cultures were maintained in lysogeny broth (LB) [41].

Peptide library screening

Ni3B-binding peptides were identified using a commercially available M13 bacteriophage display library (Ph.D.-7; New England Biolabs) with random 7-mer peptides. The DNA sequences of the 7-mer peptides are N-terminal fusions to the minor coat protein p3 of the bacteriophage M13. A short linker sequence (GGGS) separates each random peptide from the minor coat protein p3. The phage display library consists of approximately 1.28 × 109 different peptides. The target binding, elution, and phage amplification steps were conducted according to the manufacturer’s instructions. 20 mg of amorphous or crystalline Ni3B nanoparticles were used as targets. The targets were washed three-times with Tris-buffered saline (TBS, 50 mM Tris–HCl, pH 7, and 150 mM NaCl) and blocked with TBS supplemented with 5 mg/ml of BSA for 1 hour. The blocked targets were then washed three-times with TBS. To each target, a total number of 2 × 1011 phage in 1 ml of TBS with 0.1% Tween-20 (0.1% TBST) were incubated for 1 hour. Non-specifically or weakly bound phage particles were removed by washing ten-times with 0.1% TBST. The remaining bound phage particles were eluted with a solution containing 0.2 M glycine-HCl, pH 2.2 and 1 mg/ml BSA. After centrifugation, the supernatant was removed from the target and neutralised with 1 M of Tris–HCl, pH 9. The eluted phage were amplified through infection into E. coli ER2738, followed by purification by precipitation with polyethylene glycol according to the manufacturer’s instructions. This completed a round of panning. The entire biopanning process was repeated five rounds to enrich for tight binders. To inhibit the hydrophobic interactions between the phage library and the Ni3B targets, the concentration of Tween-20 was successively increased in each panning step from 0.1%, 0.3%, 0.5%, 0.6%, and 0.8%, respectively. After the fourth and fifth round of screening, the eluted phage were diluted and titrated on LB agar plates containing 5-bromo-4-chloro-3-indolyl-β-D-galactopyranoside (Xgal) and isopropyl-β-D-thiogalactopyranosid (IPTG). A total of 58 randomly selected phage plaques, which appeared blue, were picked and analysed by DNA sequencing. The phage titer was determined by titration according to manufacturer’s recommendations using appropriate dilutions of the precipitated phage.

Binding affinity assays

The binding affinity of each identified phage clone with the Ni3B substrates was demonstrated by mixing equivalent phage amounts (1 × 1010 pfu/ml) of individual phage clones with either 20 mg of amorphous or crystalline Ni3B nanoparticles in 1 ml of TBS containing 0.8% Tween-20. After 1 hour incubation at room temperature the unbound phage were removed by washing the substrates ten-times. Bound phage were then isolated using the standard acidic elution method as used in the screening procedure. For each clone, the bound phage amount was elucidated by titration according to manufacturer’s recommendations using appropriate dilutions of the eluted phage. The binding strength of a single clone directly correlates with the phage titer of the eluted phage. The assay was repeated three-times for each clone and the elucidated phage titers were arithmetically averaged. M13KE wild-type phage, with no random peptides displayed on the p3 protein, was used as a control.

Competitive binding assays

The phages with the highest binding affinity to either amorphous or crystalline Ni3B were evaluated by the method of a competitive binding assay. For this assay, the individual phage clones of the nine strongest binders on amorphous Ni3B as determined by binding affinity assays, were separately amplified and diluted into a mini-phage library at a concentration of 1 × 107 pfu/μl per clone. Subsequently 1 × 1010 pfu/ml of this minimised phage library was applied to amorphous or crystalline Ni3B nanoparticles as described for the procedure of the binding affinity assays. After a single panning round, the weakly bound phages were removed by washing the substrates and the remaining strongly bound phages were isolated using the standard acidic elution method as used in the screening procedure. The eluted phages were quantified by titration according to the manufacturer’s recommendations. The assay was repeated three-times for each substrate. A total number of 29 plaques were randomly picked for each substrate and sequenced to reveal the most strongly binding peptide sequences.

Synthesis and characterisation of amorphous and crystalline Ni3B

The Ni3B nanoparticles were synthesised from NaBH4 (Alfa Aesar, 97%) and NiCl2 × 6 H2O (Grüssing GmbH, 98%) in aqueous solution at about 0°C following a synthesis route described earlier [5]. According to this procedure amorphous Ni3B is formed primarily, which is transformed into the crystallised Ni3B sample at 490°C in vacuum (5 × 10-3 mbar, 18 h). The X-ray diffraction pattern of the annealed, crystalline sample allows for its identification as Ni3B (see Additional file 1). In previous work, we have shown using methods like X-ray diffraction, energy-dispersive X-ray spectroscopy, X-ray absorption spectroscopy, scanning and transmission electron microscopy, and energy-loss electron spectroscopy that the corresponding amorphous phase actually consists of the same boride as the crystalline modification [5, 7]. For the phage display the amorphous Ni3B nanoparticles were used after extensive washing with deionized water and drying in a desiccator under vacuum. The crystalline nanoparticles were obtained from the amorphous product after the annealing process and used directly.

Fluorescence microscopy analysis

The binding of M13 phage to amorphous and crystalline nickel boride nanoparticles was characterised with a Zeiss Axiovert 200 inverted fluorescence microscope equipped with a Zeiss AxioCam HRm. The fluorescence images were taken using emission at 528 nm. M13 phage were incubated with 10 mg of amorphous and crystalline Ni3B nanoparticles at a concentration of 3 × 1012 pfu/ml in 1 ml TBS supplemented with 0.8% Tween-20. After 2 h at room temperature, unbound phage were removed by washing the substrates three-times with TBS. Subsequently, the substrates were blocked with TBS supplemented with 2% BSA and 0.05% Tween-20 for 1 hour and washed three-times with TBS supplemented with 0.05% Tween-20. The samples were dyed using a FITC tagged anti-M13 monoclonal antibody against phage coat protein p8 (Acris Antibodies, Inc., Herford, Germany). Each target was incubated for 1 hour with 1 μg/ml of labeled monoclonal antibodies in TBS with 0.05% Tween-20. After removing unbound antibodies by washing the samples three-times with TBS containing 0.05% Tween-20, the samples were analysed by fluorescence microscopy.

Atomic force microscopy (AFM) analysis

Ni3B nanoparticles, phages and compounds of phages with Ni3B were characterised with an atomic force microscope (AFM). The measurements were carried out on a Dimension Icon AFM with a Nanoscope V controller (Bruker, Santa Barbara, California) in ambient conditions. The measurements were performed in tapping mode, to minimise the lateral interaction. Silicon cantilevers (PPP NCH, Nanosensors) with a nominal resonance frequency of 330 kHz, spring constant of 42 Nm-1, and a nominal tip diameter of less than 10 nm were used. All images were taken at a resolution of 512 × 512 pixel2. M13 phages were incubated with 10 mg of amorphous and crystalline Ni3B nanoparticles at a concentration of 3 × 1012 pfu/ml in 1 ml TBS supplemented with 0.8% Tween-20. After 2 h, unbound phages were removed by washing the substrates three-times with TBS. Samples were prepared by dropping the sample suspension on a silicon wafer or freshly cleaved mica. The samples were dried in a stream of dry nitrogen. Image analysis and processing was performed with the Nanoscope Analysis software Version 1.40 (Bruker). A plane correction procedure and a line by line fit were used to compensate for the sample tilt.

References

  1. Schwarzkopf P, Kieffer R: Refractory Hard Metals. 1953, The Macmillan Company: New York, 311-312. 1

    Google Scholar 

  2. Buzea C, Yamashita T: Review of the superconducting properties of MgB2. Supercond Sci Technol. 2001, 14: R115-R146. 10.1088/0953-2048/14/11/201.

    Article  CAS  Google Scholar 

  3. Herbst JF, Croat JJ: Neodymium-iron-boron permanent magnets. J Magn Magn Mater. 1991, 100: 57-78. 10.1016/0304-8853(91)90812-O.

    Article  CAS  Google Scholar 

  4. Brown HC, Brown CA: New, highly active metal catalysts for the hydrolysis of borohydride. J Am Chem Soc. 1962, 84: 1493-1494.

    Article  CAS  Google Scholar 

  5. Kapfenberger C, Hofmann K, Albert A: Room-temperature synthesis of metal borides. J Solid State Sci. 2003, 5: 925-930. 10.1016/S1293-2558(03)00117-1.

    Article  CAS  Google Scholar 

  6. Caputo R, Guzzetta F, Angerhofer A: Room-temperature synthesis of nickel borides via decomposition of NaBH4 promoted by nickel bromide. Inorg Chem. 2010, 49: 8756-8762. 10.1021/ic100896a.

    Article  CAS  Google Scholar 

  7. Rades S, Kornowski A, Weller H, Albert B: Wet-chemical synthesis of nanoscale iron boride. Chem Phys Chem. 2011, 12: 1756-1760. 10.1002/cphc.201001072.

    CAS  Google Scholar 

  8. Chen CL, Rosi NL: Peptide-based methods for the preparation of nanostructured inorganic materials. Angew Chem Int Ed. 2010, 49: 1924-1942. 10.1002/anie.200903572.

    Article  CAS  Google Scholar 

  9. Boar RB, Hawkins DW, McGhie JF, Barton DHR: Some applications of nickel boride as a desulphurising agent. An improved route to triterpene 2-enes. J Chem Soc, Perkin Trans. 1973, 1: 654-657.

    Article  Google Scholar 

  10. Sarma DN, Sharma RP: Nickel boride reductive cleavage of allylic trimethylsilyl ethers. Tetrahedr Lett. 1985, 26: 371-372. 10.1016/S0040-4039(01)80820-0.

    Article  CAS  Google Scholar 

  11. Seltzmann HH, Berrang BD: Nickel boride reduction of aryl nitro compounds. Tetrahedr Lett. 1993, 34: 3083-3086. 10.1016/S0040-4039(00)93385-9.

    Article  Google Scholar 

  12. Molvinger K, Lopez M, Court J: Enantioselective borane reduction of ketones with oxazaborolidines boron-bound to nickel boride nanoparticles. Tetrahedr Lett. 1999, 40: 8375-8378. 10.1016/S0040-4039(99)01871-7.

    Article  CAS  Google Scholar 

  13. Saxena I, Borah R, Sarma JC: Reductive amination of aromatic aldehydes and ketones with nickel boride. J Chem Soc, Perkin Trans. 2000, 1: 503-504.

    Article  Google Scholar 

  14. Brown CA: Catalytic hydrogenation. V. The reaction of sodium borohydride with aqueous nickel salts. P-1 nickel boride, a convenient, highly active nickel hydrogenation catalyst. J Org Chem. 1970, 35: 1900-1904. 10.1021/jo00831a039.

    Article  CAS  Google Scholar 

  15. Pavlik JW: Catalytic hydrogenation using nickel boride. J Chem Educ. 1972, 49: 528-10.1021/ed049p528.

    Article  CAS  Google Scholar 

  16. Bratkovsky AM, Rashkeev SN, Wendin G: Electronic structure, ferromagnetism, and EELS spectra of crystalline alloys FenB and NinB (n = 1, 2, 3): Aspects of universal behavior. Phys Rev B. 1993, 48: 6260-6270. 10.1103/PhysRevB.48.6260.

    Article  CAS  Google Scholar 

  17. Schaefer ZL, Ke X, Schiffer P, Schaak RE: Direct solution synthesis, reaction pathway studies, and structural characterization of crystalline Ni3B nanoparticles. J Phys Chem C. 2008, 112: 19846-19851. 10.1021/jp8082503.

    Article  CAS  Google Scholar 

  18. Sarikaya M, Tamerler C, Jen AKY, Schulten K, Baneyx F: Molecular biomimetics: nanotechnology through biology. Nat Mater. 2003, 2: 577-585. 10.1038/nmat964.

    Article  CAS  Google Scholar 

  19. Baneyx F, Schwartz DT: Selection and analysis of solid-binding peptides. Curr Opin Biotechnol. 2007, 18: 312-317. 10.1016/j.copbio.2007.04.008.

    Article  CAS  Google Scholar 

  20. Whyburn GP, Li Y, Huang Y: Protein and protein assembly based material structures. J Mater Chem. 2008, 18: 3755-3762. 10.1039/b807421f.

    Article  CAS  Google Scholar 

  21. Smith GP, Petrenko VA: Phage Display. Chem Rev. 1997, 97: 391-410. 10.1021/cr960065d.

    Article  CAS  Google Scholar 

  22. Naik RR, Stringer SJ, Agarwal G, Jones SE, Stone MO: Biomimetic synthesis and patterning of silver nanoparticles. Nat Mater. 2002, 1: 169-172. 10.1038/nmat758.

    Article  CAS  Google Scholar 

  23. Heinz H, Farmer BL, Pandey RB, Slocik JM, Patnaik SS, Pachter R, Naik RR: Nature of molecular interactions of peptides with gold, palladium, and Pd-Au bimetal surfaces in aqueous solution. J Am Chem Soc. 2009, 131: 9704-9714. 10.1021/ja900531f.

    Article  CAS  Google Scholar 

  24. Umetsu M, Mizuta M, Tsumoto K, Ohara S, Takami S, Watanabe H, Kumagai I, Adschiri T: Bioassisted room-temperature immobilization and mineralization of zinc oxide - The structural ordering of ZnO nanoparticles into a flower-type morphology. Adv Mater. 2005, 17: 2571-2575. 10.1002/adma.200500863.

    Article  CAS  Google Scholar 

  25. Rothenstein D, Claasen B, Omiecienski B, Lammel P, Bill J: Isolation of ZnO-binding 12-mer peptides and determination of their binding epitopes by NMR spectroscopy. J Am Chem Soc. 2012, 134: 12547-12556. 10.1021/ja302211w.

    Article  CAS  Google Scholar 

  26. Naik RR, Brott LL, Clarson SJ, Stone MO: Silica-precipitating peptides isolated from a combinatorial phage display peptide library. J Nanosci Nanotechnol. 2002, 2: 95-100. 10.1166/jnn.2002.074.

    Article  CAS  Google Scholar 

  27. Dickerson MB, Jones SE, Cai Y, Ahmad G, Naik RR, Kröger N, Sandhage KH: Identification and design of peptides for the rapid, high-yield formation of nanoparticulate TiO2 from aqueous solutions at room temperature. Chem Mater. 2008, 20: 1578-1584. 10.1021/cm071515t.

    Article  CAS  Google Scholar 

  28. Lee SW, Mao C, Flynn CE, Belcher AM: Ordering of quantum dots using genetically engineered viruses. Science. 2002, 296: 892-895. 10.1126/science.1068054.

    Article  CAS  Google Scholar 

  29. Flynn CE, Mao CB, Hayhurst A, Williams JL, Georgiou G, Iverson B, Belcher AM: Synthesis and organization of nanoscale II-VI semiconductor materials using evolved peptide specificity and viral capsid assembly. J Mater Chem. 2003, 13: 2414-2421. 10.1039/b307593a.

    Article  CAS  Google Scholar 

  30. Dong J, Chuan L, Zhang J, Xin ZT, Yang G, Gao B, Mao CQ, Liu NL, Shao NS, Fan M, Xue YN: Selection of novel nickel-binding peptides from flagella displayed secondary peptide library. Chem Biol Drug Des. 2006, 68: 107-112. 10.1111/j.1747-0285.2006.00421.x.

    Article  CAS  Google Scholar 

  31. Chung KCC, Cao L, Dias AV, Pickering IJ, George GN, Zamble DB: A high-affinity metal-binding peptide from Escherichia coli HypB. J Am Chem Soc. 2008, 130: 14056-14057. 10.1021/ja8055003.

    Article  CAS  Google Scholar 

  32. Zoroddu MA, Medici S, Peana M: Copper and nickel binding in multi-histidinic peptide fragments. J Inorg Biochem. 2009, 103: 1214-1220. 10.1016/j.jinorgbio.2009.06.008.

    Article  CAS  Google Scholar 

  33. Thomas CJ, Sharama S, Kumar G, Visweswariah SS, Surolia A: Biopanning of endotoxin-specific phage displayed peptides. Biochem Biophys Res Commun. 2003, 307: 133-138. 10.1016/S0006-291X(03)01136-7.

    Article  CAS  Google Scholar 

  34. Okamoto Y, Nitta Y, Imanaka T: Surface characterisation of nickel boride and nickel phosphide catalysts by X-ray photoelectron spectroscopy. J Chem Soc, Faraday Trans. 1978, 1: 2027-2039.

    Google Scholar 

  35. Jaworski JW, Raorane D, Huh JH, Majumdar A, Lee SW: Evolutionary screening of biomimetic coatings for selective detection of explosives. Langmuir. 2008, 24: 4938-4943. 10.1021/la7035289.

    Article  CAS  Google Scholar 

  36. Willett RL, Baldwin KW, West KW, Pfeiffer LN: Differential adhesion of amino acids to inorganic surfaces. PNAS. 2005, 102: 7817-7822. 10.1073/pnas.0408565102.

    Article  CAS  Google Scholar 

  37. Amaral M, Lopes MA, Santos JD, Silva RF: Wettability and surface charge of Si3N4-bioglass composites in contact with simulated physiological liquids. Biomaterials. 2002, 23: 4123-4129. 10.1016/S0142-9612(02)00155-2.

    Article  CAS  Google Scholar 

  38. Fahrenholtz WG, Hilmas GE, Talmy IG, Zaykoski JA: Refractory diborides of zirconium and hafnium. J Am Ceram Soc. 2007, 90: 1347-1364. 10.1111/j.1551-2916.2007.01583.x.

    Article  CAS  Google Scholar 

  39. Brown D, Ma B-M, Chen Z: Developments in the processing and properties of NdFeB-type permanent magnets. J Magn Magn Mater. 2002, 248: 432-440. 10.1016/S0304-8853(02)00334-7.

    Article  CAS  Google Scholar 

  40. Nagamatsu J, Nakagawa N, Muranaka T, Zenitani Y, Akimitsu J: Superconductivity at 39 K in magnesium diboride. Nature. 2001, 410: 63-64. 10.1038/35065039.

    Article  CAS  Google Scholar 

  41. Bertani G: Studies on lysogenesis. I. The mode of phage liberation by lysogenic Escherichia coli. J. Bacteriol. 1951, 62: 293-300.

    CAS  Google Scholar 

Download references

Acknowledgements

This work was supported by the Deutsche Forschungsgemeinschaft (DFG) under grant HA 1251/2-1, STA 1026/5-1, and AL 536/11-1 as part of the Priority Programme SPP 1569 “Generation of multifunctional inorganic materials by molecular bionics”.

Author information

Authors and Affiliations

  1. Institute of Technical Biochemistry, University of Stuttgart, Allmandring 31, 70569, Stuttgart, Germany

    Martin Ploss, Sandra J Facey & Bernhard Hauer

  2. Eduard-Zintl-Institute of Inorganic and Physical Chemistry, Technische Universität Darmstadt, Alarich-Weiss-Str. 12, 64287, Darmstadt, Germany

    Carina Bruhn, Kathrin Hofmann & Barbara Albert

  3. Center of Smart Interfaces, Physics of Surfaces and Institute of Materials Sciences, Technische Universität Darmstadt, Alarich-Weiss-Str. 10, 64287, Darmstadt, Germany

    Limor Zemel & Robert W Stark

Authors
  1. Martin Ploss
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Sandra J Facey
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. Carina Bruhn
    View author publications

    You can also search for this author in PubMed Google Scholar

  4. Limor Zemel
    View author publications

    You can also search for this author in PubMed Google Scholar

  5. Kathrin Hofmann
    View author publications

    You can also search for this author in PubMed Google Scholar

  6. Robert W Stark
    View author publications

    You can also search for this author in PubMed Google Scholar

  7. Barbara Albert
    View author publications

    You can also search for this author in PubMed Google Scholar

  8. Bernhard Hauer
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to Bernhard Hauer.

Additional information

Competing interests

The authors declare that they have no competing interests.

Authors’ contributions

SJF and MP drafted the manuscript. CB and KH synthesised the Ni3B substrates for the use in biopanning. MP identified and characterised the binding peptides, and visualised the adhesion of the phage by fluorescence microscopy. LZ did the AFM analysis of Ni3B nanoparticles, phages and compounds of phages with Ni3B. BA, SJF, RWS, and BH planned and designed this project. SJF, MP and BA read and approved the final manuscript. All authors read and approved the final manuscript.

Electronic supplementary material

12896_2013_890_MOESM1_ESM.pdf

Additional file 1: X-ray powder diffraction profile. Calculated (solid blue line) and difference (solid red line) X-ray powder diffraction profiles for the Rietveld refinement of crystalline Ni3B. Reflection positions are marked (blue bars). (PDF 56 KB)

Authors’ original submitted files for images

Rights and permissions

Open Access This article is published under license to BioMed Central Ltd. This is an Open Access article is distributed under the terms of the Creative Commons Attribution License ( https://creativecommons.org/licenses/by/2.0 ), which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

Reprints and permissions

About this article

Cite this article

Ploss, M., Facey, S.J., Bruhn, C. et al. Selection of peptides binding to metallic borides by screening M13 phage display libraries. BMC Biotechnol 14, 12 (2014). https://doi.org/10.1186/1472-6750-14-12

Download citation

  • Received:

  • Accepted:

  • Published:

  • DOI: https://doi.org/10.1186/1472-6750-14-12

Keywords

BMC Biotechnology

ISSN: 1472-6750

Contact us